Pengaruh Variasi Temperatur Artificial Aging Terhadap Kekerasan Aluminium 6061 Daur Ulang

Beny Hartawan, Teuku Marjuni, Anang Ansyori, Adi Prastyo

Abstract


Recycling is an effective way of utilising scrab ships waste in aluminium 6061. One of the alternative ways of utilisation is by casting. Increasing the hardness of the material after casting is done by artificial aging. The purpose of the study was to determine the material of the castings after the aging process. The research method was sand casting, 450°C heat treatment, quenching with (used) oil cooling media and artificial aging at 190°C with varying resistance times of 1, 5 and 11 hours. The test results after the aging process showed an increase in hardness. The average hardness without heat treatment is 38.6 HRB, then the average hardness of sample AA 1 is 39 HRB. When compared to the average without heat treatment and after aging, it has increased by 1.03%. Then, the average hardness of sample AA 5 is 45 HRB, which is greater than the hardness value of AA 1 hour. Meanwhile, the average hardness of sample AA 11 experienced a decrease in hardness of 40.4 HRB. Structural observations of samples without heat treatment have quite large pores and porosity. The addition of holding time during aging is thought to have no effect on grain size, but changes the grain shape. At the grain boundary of the aluminium matrix, the alloying element Si forms a precipitate that is thought to be a Mg2Si compound. This precipitate is likely to form during the aging process.A maximum 250 word abstract in English in italics with Times New Roman 11 point. Abstract should be clear, descriptive, and should provide a brief overview of the problem studied. Abstract topics include reasons for the selection or the importance of research topics, research methods and a summary of the results. Abstract should end with a comment about the importance of the results or conclusions brief.

Full Text:

PDF

References


Andoko, A. et al. (2020) ‘The effects of artificial aging temperature on tensile strength , hardness , micro- structure , and fault morphology in AlSiMg’, 98(2), pp. 49–55. doi: 10.5604/01.3001.0014.1480.

Anne Zulfia1, Ratna Juwita1, Ari Uliana1, I Nyoman Jujur dan Jarot Raharjo. Proses Penuaan (Aging) pada Paduan Aluminium AA 333 Hasil Proses Sand Casting. Fakultas Teknik Universitas Indonesia, Jakarta

Beny Hartawan, Zulhanif dan Harnowo Supriadi, 2018. Analisis Pengaruh Perlakuan Panas Artificial Aging pada Aluminium Magnesium Silikon (Al-Mg-Si) yang Dicor Ulang Terhadap Sifat Mekanis. Jurusan Teknik Mesin, Fakultas Teknik Universitas Lampung

Callister, Jr., William, D., 2007. “Materials Science and Engineering an Introduction”, 7 ed., John Wiley & Sons, Inc., New York. Concise Desktop Reference 2 ed., Springer.

D. Zhang, L. Zheng, and D. St. John, Effect of a Short Solution Treatment Time on Microstructure and Mechanical Properties of Modifi ed Al7wt.% Si- 0.3wt.%Mg Alloy, Journal of Light Metals, 2, pp. 27–36, 2002.

Fauzi Widyawati1* , Muhammad Miftah Solahudin2 , Syamsul Hidayat3. Analisis Variasi Temperatur Artificial aging terhadap Struktur Mikro dan Sifat Mekanik pada Aluminium 6061 T6. Program Studi Teknik Metalurgi, Fakultas Teknologi Lingkungan dan Mineral, Universitas Teknologi Sumbawa. SPECTA Journal of Technology Vol 8, No 1 Juni, 2024 pg: 12 – 21

Guntur Prakoso1 (2024). Pemanfaatan Limbah B3 Scrap Aluminium (A345-2) Untuk Menjadi Bahan Baku Ingot Aluminium. Teknik Lingkungan, Universitas Pelita Bangsa. Jurnal Teknologi dan Pengelolaan Lingkungan, ISSN: 2614-2635. Maret 3, 2024

Nur Imam Subagyo, Zulhanif, Harnowo Supriadi, 2017. Analisis Pengaruh Artificial Aging Terhadap Sifat Mekanis Pada Aluminium Seri 6061. Seminar Nasional Energi dan Industri Manufaktur SIGER 2017; Universitas Lampung, 7-8 November 2017.

Parwening Sabdo Hermawan, Helmy Purwanto, Sri M. B. Respati. Analisa Pengaruh Variasi Temperatur Tuang pada Pengecoran Squeeze Terhadap Struktur Mikro dan Kekerasan Produk Sepatu Kampas Rem dengan Bahan Aluminium (Al) Silikon (Si) Daur Ulang, 2013. Program Studi Teknik Mesin, Fakultas Teknik, Universitas Wahid Hasyim

Pradityana, Atria dan Widyantoro, K., E. 2019. Effects of Holding Time During Artificial Aging Process on AA6061 to the Mechanical Properties. IPTEK Journal of Proceedings Series. No. 3: 121-123.

Rajasekaran, S., Udayashankar, N. K. and Nayak, J. (2012) ‘T4 and T6 Treatment of 6061 Al-15 Vol . % SiC P Composite’, 2012. doi: 10.5402/2012/374719.

Rambabu, P., Prasad, N. E. and Kutumbarao, V. V (2017) ‘Aerospace Materials and Material Technologies’. doi: 10.1007/978-981-10-2143-5.

Surdia,T., dan Chijiwa,K., (2000). Teknik Pengecoran Logam, Cetakan Ke-8, PT. Pradnya Paramita, Jakarta.

Susiana, A., Leon Habibi, M., Kelautan dan Perikanan Kupang Jalan Kampung Baru Kupang Barat, P., & Tenggara Timur, N. (2021). Karakterisasi Recycle Aluminium Scrap Untuk Piston. Jurnal Ilmiah Program Studi Magister Teknik Mesin (Vol. 11, Nomor 2).

S. Shivkumar et al., Influence of Solution Treatment on Tensile Properties of Sr Modifi ed Al-Si-Mg Alloys, Journal of Heat Treating, 8, pp. 63–70, 1990.

Tsamroh, D. I. et al. (2018) ‘Optimization of multistage artificial aging parameters on Al-Cu alloy mechanical properties’, Journal of Achievements in Materials and Manufacturing Engineering, 87(2), pp. 62–67. doi: 10.5604/01.3001.0012.2828.

Tsamroh, D. I. (2021) ‘Comparison finite element analysis on duralium strength against multistage artificial aging process’, Archives of Materials Science and Engineering, 109(1), pp. 29–34. doi: 10.5604/01.3001.0015.0512.

Tsamroh, D. I. dan Muchammad Riza Fauzy2 (2022). Peningkatan Sifat Mekanik Al6061 Melalui Heat Treatment Natural-Artificial Aging. Jurusan Teknik Mesin, Fakultas Teknik, Universitas Merdeka Malang. F.SAINTEK Unira Malang | Vol. 06 | No. 1 April, 2022

Wardani, I. P. et al. (2022) ‘Pengaruh Natural Aging Sebelum Proses Artificial aging Terhadap Sifat Mekanik Aluminium 6061. Seminar Nasional Sains dan Teknologi Terapan VIII 2020, pp. 109– 114.




Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.